The mechanical behaviour of implantable scaffolds is of relevant interest in all applications which require load-bearing capability. This study aims at establishing a quantitative relationship between the mechanical properties of glass-ceramic scaffolds for bone repair and the nano/micro-scale properties of their constituent materials. A nanoindentation study is carried out spanning different penetration depth on bulk (pore-free) glass-ceramic samples and on the walls of porous scaffolds. Micro-tomographical investigations allow assessing small-scale porosity of the scaffold walls. A simple homogenization model is used to establish the relationship between the elastic modulus of the bulk material and that of the micro-porous walls of the scaffolds. The elastic modulus of scaffold walls was found to be approximately 50% lower than that of the bulk glass-ceramic. The properties estimated experimentally on the walls of the scaffolds are quantitatively consistent with the analytical predictions provided by the homogenization model and the micro-porosity measured through tomographical analyses.
Mechanical characterization of glass-ceramic scaffolds at multiple characteristic lengths through nanoindentation
SHAHGHOLI GHAHFAROKHI, MOHAMAD;GASTALDI, DARIO;VENA, PASQUALE
2016-01-01
Abstract
The mechanical behaviour of implantable scaffolds is of relevant interest in all applications which require load-bearing capability. This study aims at establishing a quantitative relationship between the mechanical properties of glass-ceramic scaffolds for bone repair and the nano/micro-scale properties of their constituent materials. A nanoindentation study is carried out spanning different penetration depth on bulk (pore-free) glass-ceramic samples and on the walls of porous scaffolds. Micro-tomographical investigations allow assessing small-scale porosity of the scaffold walls. A simple homogenization model is used to establish the relationship between the elastic modulus of the bulk material and that of the micro-porous walls of the scaffolds. The elastic modulus of scaffold walls was found to be approximately 50% lower than that of the bulk glass-ceramic. The properties estimated experimentally on the walls of the scaffolds are quantitatively consistent with the analytical predictions provided by the homogenization model and the micro-porosity measured through tomographical analyses.File | Dimensione | Formato | |
---|---|---|---|
JECS-2016.pdf
Accesso riservato
:
Publisher’s version
Dimensione
1 MB
Formato
Adobe PDF
|
1 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.