In order to investigate the effect of twinning–detwinning on the mechanical properties of AZ31 extruded magnesium alloy pre-compression and pre-stretch deformation were conducted along extrusion direction (ED) at 1%, 3%, 5% strain levels. After pre-strain, the strain-path was inverted by performing tensile or compressive tests at room temperature. Results showed that the detwinning behavior occurred during the inverse tension after the pre-compression. Although due to the aforementioned effect the tensile yield strength decreased, by increasing the pre-compressive levels both fracture elongation and peak strength improved. In the inverse compressive tests after pre-stretch the {1012} twinning was restrained and the volume fraction of twins decreased, leading to the improvement of yield strength by increasing in pre-stretching levels.
The effect of twinning and detwinning on the mechanical property of AZ31 extruded magnesium alloy during strain-path changes
MOSTAED, EHSAN;VEDANI, MAURIZIO;
2014-01-01
Abstract
In order to investigate the effect of twinning–detwinning on the mechanical properties of AZ31 extruded magnesium alloy pre-compression and pre-stretch deformation were conducted along extrusion direction (ED) at 1%, 3%, 5% strain levels. After pre-strain, the strain-path was inverted by performing tensile or compressive tests at room temperature. Results showed that the detwinning behavior occurred during the inverse tension after the pre-compression. Although due to the aforementioned effect the tensile yield strength decreased, by increasing the pre-compressive levels both fracture elongation and peak strength improved. In the inverse compressive tests after pre-stretch the {1012} twinning was restrained and the volume fraction of twins decreased, leading to the improvement of yield strength by increasing in pre-stretching levels.File | Dimensione | Formato | |
---|---|---|---|
twin detwin mater design 2014.pdf
Accesso riservato
:
Publisher’s version
Dimensione
4.08 MB
Formato
Adobe PDF
|
4.08 MB | Adobe PDF | Visualizza/Apri |
The effect of twinning and detwinning on the mechanical property of AZ31_11311-971336_Vedani.pdf
accesso aperto
:
Post-Print (DRAFT o Author’s Accepted Manuscript-AAM)
Dimensione
3.96 MB
Formato
Adobe PDF
|
3.96 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.