Chemical reactions between carbon steel, water and chemical species produce corrosion layers (scales) on the internal surface of pipelines transporting hydrocarbons. Scales act as a diffusion barrier and prevent the progress of corrosion, a dangerous failure initiator. The protective film (10-100 m thickness) can be removed locally by the action of the internal flow, or by other mechanisms. Adhesion with the substrate and the failure modes of the corrosion layer can be tested by indentation. Some results are presented of experiments performed on specimens with scales grown in a controlled environment.
An investigation on corrosion protection layers in pipelines transporting hydrocarbons
BOLZON, GABRIELLA;
2014-01-01
Abstract
Chemical reactions between carbon steel, water and chemical species produce corrosion layers (scales) on the internal surface of pipelines transporting hydrocarbons. Scales act as a diffusion barrier and prevent the progress of corrosion, a dangerous failure initiator. The protective film (10-100 m thickness) can be removed locally by the action of the internal flow, or by other mechanisms. Adhesion with the substrate and the failure modes of the corrosion layer can be tested by indentation. Some results are presented of experiments performed on specimens with scales grown in a controlled environment.File in questo prodotto:
File | Dimensione | Formato | |
---|---|---|---|
ggb FraIntStr14.pdf
accesso aperto
:
Post-Print (DRAFT o Author’s Accepted Manuscript-AAM)
Dimensione
4.84 MB
Formato
Adobe PDF
|
4.84 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.