The reactivity parameters of the copolymerization of N,N-bis(2-methacryloyloxyethyl)-p-toluidine (BMAT) (M1) with methyl methacrylate (MMA) (M2) in 1,4-dioxane, i.e. r1 = 1.07 ± 0.20, and r2 = 0.11 ± 0.19, and with bisphenol-A bis(2-hydroxypropyl methacrylate) (Bis-GMA) (M2) in benzene, i.e. r1 = 0.58 ± 0.04, and r2 = 0.03 ± 0.03, were determined at 60°C at low concentration and low conversion (∼5%) of the monomers. Strongly delayed gelation occurred during the copolymerization of BMAT and MMA at monomer conversions of 20–30%, relatively independently of the composition of the monomer mixture. The efficiency of BMAT and N-acryloyl-N′-phenylpiperazine as activators in the redox initiated copolymerization of Bis-GMA in dental composites at ambient temperatures was found to be comparatively low. In the case where BMAT was used in equimolar proportions to benzoyl peroxide the former component was not detectable in the extract of the cured composite

Copolymerization and activation of peroxide decomposition with acrylic derivatives of tertiary aromatic amines

TANZI, MARIA CRISTINA
1994-01-01

Abstract

The reactivity parameters of the copolymerization of N,N-bis(2-methacryloyloxyethyl)-p-toluidine (BMAT) (M1) with methyl methacrylate (MMA) (M2) in 1,4-dioxane, i.e. r1 = 1.07 ± 0.20, and r2 = 0.11 ± 0.19, and with bisphenol-A bis(2-hydroxypropyl methacrylate) (Bis-GMA) (M2) in benzene, i.e. r1 = 0.58 ± 0.04, and r2 = 0.03 ± 0.03, were determined at 60°C at low concentration and low conversion (∼5%) of the monomers. Strongly delayed gelation occurred during the copolymerization of BMAT and MMA at monomer conversions of 20–30%, relatively independently of the composition of the monomer mixture. The efficiency of BMAT and N-acryloyl-N′-phenylpiperazine as activators in the redox initiated copolymerization of Bis-GMA in dental composites at ambient temperatures was found to be comparatively low. In the case where BMAT was used in equimolar proportions to benzoyl peroxide the former component was not detectable in the extract of the cured composite
1994
copolymerization, redox initiation, dental composite
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11311/668036
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact