3-Methyl-1,3-pentadiene was polymerized with the system Fe(bipy)2Cl2−MAO (bipy = bipyridine) obtaining a highly stereoregular polymer. The polymer was completely characterized by IR, NMR (13C, 1H in solution and 13C in the solid state), DSC, and X-ray techniques and found to have a syndiotactic E-1,2 structure. The crystalline structure of the polymer was also determined, and comparisons are made with other crystalline 1,2-polydienes. The results were compared with those obtained from other dienes (butadiene, isoprene, 2,3-dimethyl-1,3-butadiene) with the same catalyst, which allowed for new data confirming and supporting what already proposed to interpret the diene polymerization mechanism.
Synthesis and characterization of syndiotactic 1,2-poly(3-methyl-1,3-pentadiene)
GIARRUSSO, ANTONINO;PORRI, LIDO
2007-01-01
Abstract
3-Methyl-1,3-pentadiene was polymerized with the system Fe(bipy)2Cl2−MAO (bipy = bipyridine) obtaining a highly stereoregular polymer. The polymer was completely characterized by IR, NMR (13C, 1H in solution and 13C in the solid state), DSC, and X-ray techniques and found to have a syndiotactic E-1,2 structure. The crystalline structure of the polymer was also determined, and comparisons are made with other crystalline 1,2-polydienes. The results were compared with those obtained from other dienes (butadiene, isoprene, 2,3-dimethyl-1,3-butadiene) with the same catalyst, which allowed for new data confirming and supporting what already proposed to interpret the diene polymerization mechanism.File | Dimensione | Formato | |
---|---|---|---|
Macromoleculs.pdf
Accesso riservato
:
Post-Print (DRAFT o Author’s Accepted Manuscript-AAM)
Dimensione
196.31 kB
Formato
Adobe PDF
|
196.31 kB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.