Well-oriented permanent magnets of CoPtW(P) alloys with the basal plane parallel to the surface and a columnar structure were obtained by electrodeposition. Relatively high saturation moments and coercivities, both in perpendicular and in parallel magnetic field, are obtained at thickness up to 20 μm. Temperature dependence was also investigated, showing a great decrease of the magnetic properties. Chemical post-treatments can strongly influence magnetic properties, decreasing saturation magnetisation and coercivity while increasing squareness ratio.

Electrodeposition of micromagnets of CoPtW(P) alloys

FRANZ, SILVIA;BESTETTI, MASSIMILIANO;CAVALLOTTI, PIETRO LUIGI
2002-01-01

Abstract

Well-oriented permanent magnets of CoPtW(P) alloys with the basal plane parallel to the surface and a columnar structure were obtained by electrodeposition. Relatively high saturation moments and coercivities, both in perpendicular and in parallel magnetic field, are obtained at thickness up to 20 μm. Temperature dependence was also investigated, showing a great decrease of the magnetic properties. Chemical post-treatments can strongly influence magnetic properties, decreasing saturation magnetisation and coercivity while increasing squareness ratio.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11311/557513
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact