The corrosion of reinforcing bars (rebars) is the main cause of premature failure on reinforced concrete structures. The ingress of chlorides and the carbonation process that leads to neutralisation of alkaline pore solution are among the key phenomena promoting such corrosion. This paper deals with the effectiveness of commercial corrosion inhibitors to prevent corrosion of reinforcements in concrete. Three organic inhibitors and, by comparison, a calcium nitrite based product were added to fresh concrete in dosage suggested by producers. Experimental tests were carried out both in chlorides contaminated concrete (produced by adding chlorides directly to the mixture or by penetrating hardened concrete using ponding cycles) and in carbonated concrete. In order to study the effectiveness of the inhibitors on the initiation of corrosion, measurements were made over two years of two electrochemical parameters, the free corrosion potential and the polarisation resistance. These are discussed and compared with the results obtained for concrete specimens without inhibitors. One of the organic corrosion inhibitor and nitrite based product both delayed the initiation of corrosion.

Corrosion inhibitors in reinforced concrete structures. Part 1: preventative technique

BOLZONI, FABIO MARIA;GOIDANICH, SARA;LAZZARI, LUCIANO;ORMELLESE, MARCO;PEDEFERRI, MARIAPIA
2004-01-01

Abstract

The corrosion of reinforcing bars (rebars) is the main cause of premature failure on reinforced concrete structures. The ingress of chlorides and the carbonation process that leads to neutralisation of alkaline pore solution are among the key phenomena promoting such corrosion. This paper deals with the effectiveness of commercial corrosion inhibitors to prevent corrosion of reinforcements in concrete. Three organic inhibitors and, by comparison, a calcium nitrite based product were added to fresh concrete in dosage suggested by producers. Experimental tests were carried out both in chlorides contaminated concrete (produced by adding chlorides directly to the mixture or by penetrating hardened concrete using ponding cycles) and in carbonated concrete. In order to study the effectiveness of the inhibitors on the initiation of corrosion, measurements were made over two years of two electrochemical parameters, the free corrosion potential and the polarisation resistance. These are discussed and compared with the results obtained for concrete specimens without inhibitors. One of the organic corrosion inhibitor and nitrite based product both delayed the initiation of corrosion.
2004
File in questo prodotto:
File Dimensione Formato  
BCJ - mixed inhib - 2004.pdf

Accesso riservato

: Altro materiale allegato
Dimensione 1.09 MB
Formato Adobe PDF
1.09 MB Adobe PDF   Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11311/555867
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 33
  • ???jsp.display-item.citation.isi??? 28
social impact