Shape memory polyurethanes (SMPUs) represent promising candidate materials for aneurysm embolization, since they could enable clinical problems still associated with these clinical procedures to be overcome. In this work, we report on the characterization of physicochemical, thermomechanical and in vitro interface properties of two SMPU foams (Cold Hibernated Elastic Memory, CHEM), proposed as a material for embolization devices in minimally invasive procedures. Moreover, because device sterilization is mandatory for in vivo applications, effects on the properties of the foams after plasma sterilization were also evaluated. Both foams (CHEM 3520 and CHEM 5520) showed excellent shape recovery ability (recovery rate, Rr, up to 99%) in conventional shape recovery tests, performed at constant heating rate. Transition temperatures (Ttrans), determined by tand peaks in dynamic mechanical analysis (DMA), were 32.2 and 45.1 C, for CHEM 3520 and 5520, respectively. The value of Ttrans affects shape memory ability in the recovery test at 37 C, which simulates the behavior after implantation of the device: in fact, Rr was significantly higher for lower Ttrans foam (Rr 82% and Rr 46%, respectively, for CHEM 3520 and CHEM 5520). After plasma sterilization performed by a Sterrad sterilization system, an increase in open porosity was observed: this is probably due to the sterilization cycle; however, no effects on shape recovery behavior were observed. Furthermore, plasma treatment had no significant effect on L929 cells in in vitro cytotoxicity tests, performed on cell culture medium extracts in contact with foams for up to 7 days. Moreover, direct cytocompatibility tests showed a good colonization and growth from L929 cells on CHEM foams, suggesting the effectiveness of an in vivo healing process. All these results seem to suggest that CHEM foams could be advantageously used for manufacturing devices for mini-invasive embolization procedures of aneurysms.

Shape memory polymer foams for cerebral aneurysm reparation: Effects of plasma sterilization on physical properties and cytocompatibility

DE NARDO, LUIGI;CIGADA, ALBERTO;TANZI, MARIA CRISTINA;FARE', SILVIA
2009-01-01

Abstract

Shape memory polyurethanes (SMPUs) represent promising candidate materials for aneurysm embolization, since they could enable clinical problems still associated with these clinical procedures to be overcome. In this work, we report on the characterization of physicochemical, thermomechanical and in vitro interface properties of two SMPU foams (Cold Hibernated Elastic Memory, CHEM), proposed as a material for embolization devices in minimally invasive procedures. Moreover, because device sterilization is mandatory for in vivo applications, effects on the properties of the foams after plasma sterilization were also evaluated. Both foams (CHEM 3520 and CHEM 5520) showed excellent shape recovery ability (recovery rate, Rr, up to 99%) in conventional shape recovery tests, performed at constant heating rate. Transition temperatures (Ttrans), determined by tand peaks in dynamic mechanical analysis (DMA), were 32.2 and 45.1 C, for CHEM 3520 and 5520, respectively. The value of Ttrans affects shape memory ability in the recovery test at 37 C, which simulates the behavior after implantation of the device: in fact, Rr was significantly higher for lower Ttrans foam (Rr 82% and Rr 46%, respectively, for CHEM 3520 and CHEM 5520). After plasma sterilization performed by a Sterrad sterilization system, an increase in open porosity was observed: this is probably due to the sterilization cycle; however, no effects on shape recovery behavior were observed. Furthermore, plasma treatment had no significant effect on L929 cells in in vitro cytotoxicity tests, performed on cell culture medium extracts in contact with foams for up to 7 days. Moreover, direct cytocompatibility tests showed a good colonization and growth from L929 cells on CHEM foams, suggesting the effectiveness of an in vivo healing process. All these results seem to suggest that CHEM foams could be advantageously used for manufacturing devices for mini-invasive embolization procedures of aneurysms.
2009
Shape memory polymers; Minimally invasive structures; Plasma sterilization; Cytocompatibility; Polyurethane foams
File in questo prodotto:
File Dimensione Formato  
Acta Bio 2009.pdf

Accesso riservato

: Altro materiale allegato
Dimensione 1.13 MB
Formato Adobe PDF
1.13 MB Adobe PDF   Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11311/544547
Citazioni
  • ???jsp.display-item.citation.pmc??? 16
  • Scopus 65
  • ???jsp.display-item.citation.isi??? 56
social impact