Friction and wear performance of polyether ether ketone (PEEK) polymers in three lubrication regimes

This experimental study investigates the friction and wear of three coatings commonly used in industrial applications, particularly in hydrodynamic bearings. The three materials under investigation were Babbitt, polyether ether ketone (PEEK) reinforced with 15% carbon fibers, and PEEK reinforced with 20% carbon fibers. The first polymer material was extruded, while the other was produced by fused deposition modelling (FDM). The materials were subjected to sliding tests in a pin-on-disc configuration, with a steel ball serving as the counter surface. The tests were conducted at room temperature, with a load of 10 N and under three different lubrication conditions: dry, grease, and oil. The linear speed was set at 0.3 m/s for the dry and semi-solid lubrication tests, while for the oil tests, the speed was set at 0.25 m/s. The greases used had consistency grades of NGLI 000 and NGLI 2. An ISO VG 68 circulation oil was used for the oil lubrication tests. Additionally, thermodynamic analyses were performed under the most severe conditions (i.e., dry) to investigate the steel–Babbitt and steel–PEEK contact.