We present the fabrication and characterization of two high concentration Yb3+-Er3+ co-doped double clad phosphate glass optical fibers (named A and B for short) manufactured by preform drawing, with the preform being obtained by the rod-in-tube technique. Optical amplification was demonstrated by core pumping 27 mm of fiber A (7/25/70 μm and NA = 0.17 between core and inner cladding) with a laser diode at 976 nm, achieving a 10.7 dB internal gain, i.e., 4.0 dB cm-1, for small signal input at 1535 nm. Amplification was also demonstrated in a cladding-pumped counter propagating configuration using both fibers A and B (12/48/140 μm and NA = 0.08). A maximum internal gain of 18.5 dB was achieved with 8 cm of fiber B, corresponding to an amplification of 2.3 dB cm-1, for small signal input at 1535 nm.

High concentration Yb-Er co-doped phosphate glass for optical fiber amplification

Lousteau J.;
2015-01-01

Abstract

We present the fabrication and characterization of two high concentration Yb3+-Er3+ co-doped double clad phosphate glass optical fibers (named A and B for short) manufactured by preform drawing, with the preform being obtained by the rod-in-tube technique. Optical amplification was demonstrated by core pumping 27 mm of fiber A (7/25/70 μm and NA = 0.17 between core and inner cladding) with a laser diode at 976 nm, achieving a 10.7 dB internal gain, i.e., 4.0 dB cm-1, for small signal input at 1535 nm. Amplification was also demonstrated in a cladding-pumped counter propagating configuration using both fibers A and B (12/48/140 μm and NA = 0.08). A maximum internal gain of 18.5 dB was achieved with 8 cm of fiber B, corresponding to an amplification of 2.3 dB cm-1, for small signal input at 1535 nm.
2015
double clad fiber
optical fiber amplifier
optical fiber fabrication
phosphate glass
Yb-Er co-doped fiber
File in questo prodotto:
File Dimensione Formato  
11311-1158978_Lousteau.pdf

accesso aperto

: Post-Print (DRAFT o Author’s Accepted Manuscript-AAM)
Dimensione 1.18 MB
Formato Adobe PDF
1.18 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11311/1158978
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 46
  • ???jsp.display-item.citation.isi??? 42
social impact