Innesco e propagazione della corrosione dell’armatura in calcestruzzi fibrorinforzati ad altissime prestazioni (UHPFRC)

This note presents the preliminary results of an experimental investigation aimed at studying the corrosion behaviour of reinforcement in ultra-high performance fibre reinforced concretes. Regarding parameters related with corrosion initiation, tests of capillary absorption, water content and water absorption, electrical resistivity, accelerated carbonation and chloride migration were carried out. Results highlighted that concrete is a very impervious material. Results of corrosion tests - both on carbon steel and stainless steel reinforcements - showed conditions of passivity even after exposure to wetting and drying cycles with chlorides. Only in the presence of cracks, carbon steel reinforcement showed a possible onset of corrosion.

La memoria presenta i risultati preliminari di un’indagine sperimentale volta alla caratterizzazione del compor-tamento alla corrosione dell’armatura in calcestruzzi fibrorinforzati ad altissime prestazioni. Per la caratteriz-zazione di parametri correlati con il tempo di innesco si sono svolte prove di risalita capillare, contenuto d’ac¬qua e assorbimento, resistività elettrica, carbonatazione accelerata e migrazione di cloruri. Queste prove hanno mostrato che il calcestruzzo è un materiale molto impervio. Le prove di corrosione dell’armatura - sia di acciaio al carbonio che di acciaio inossidabile - hanno indicato condizioni di passività anche in seguito all’espo¬sizione a cicli di asciutto-bagnato con cloruri. Solo in presenza di fessure l’armatura di acciaio al carbonio ha mostrato un possibile innesco della corrosione.