Tensile properties of an Al-Si-Mg casting alloy with reduced Si content and Cr addition were investigated at room and high temperatures. It was found that the studied alloy exhibits a remarkable performance up to 200 degrees C, with comparable or slightly higher strength than typical values for Al-Si-Mg-Cu alloys, commonly used for high-temperature applications, and good elongation. This is due to the choice of proper heat treatment and to the formation of dispersoids containing Cr during heat treatment, which are stable at the considered temperatures, as demonstrated by scanning and transmission electron microscopy (STEM) analysis. Interestingly, exposure to 300 degrees C during tensile tests enhanced an additional formation of dispersoids. It is believed that heating the material in T6 condition led to such observed dispersoids formation since precursors were already present in the Al matrix. This is not sufficient to avoid material softening at 300 degrees C, but it represents an interesting point in order to develop alternative heat treatment routes for dispersion-strengthened Al alloys.
Tensile Properties of a Cast Al-Si-Mg Alloy with Reduced Si Content and Cr Addition at High Temperature
Gariboldi E.;
2019-01-01
Abstract
Tensile properties of an Al-Si-Mg casting alloy with reduced Si content and Cr addition were investigated at room and high temperatures. It was found that the studied alloy exhibits a remarkable performance up to 200 degrees C, with comparable or slightly higher strength than typical values for Al-Si-Mg-Cu alloys, commonly used for high-temperature applications, and good elongation. This is due to the choice of proper heat treatment and to the formation of dispersoids containing Cr during heat treatment, which are stable at the considered temperatures, as demonstrated by scanning and transmission electron microscopy (STEM) analysis. Interestingly, exposure to 300 degrees C during tensile tests enhanced an additional formation of dispersoids. It is believed that heating the material in T6 condition led to such observed dispersoids formation since precursors were already present in the Al matrix. This is not sufficient to avoid material softening at 300 degrees C, but it represents an interesting point in order to develop alternative heat treatment routes for dispersion-strengthened Al alloys.File | Dimensione | Formato | |
---|---|---|---|
2019 JMEP-19-05-18319.R2_Proof_hi version accepted 25 oct 2019.pdf
Accesso riservato
:
Post-Print (DRAFT o Author’s Accepted Manuscript-AAM)
Dimensione
4.25 MB
Formato
Adobe PDF
|
4.25 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.