The effective g-factor of 2D holes in modulation doped p-SiGe/Ge/SiGe structures was studied. The AC conductivity of samples with hole densities from 3.9 × 1011to 6.2 × 1011cm-2was measured in perpendicular magnetic fields up to 8 T using a contactless acoustic method. From the analysis of the temperature dependence of conductivity oscillations, the g⊥-factor of each sample was determined. The g⊥-factor was found to be decreasing approximately linearly with hole density. This effect is attributed to the non-parabolicity of the valence band.
Effective g factor of 2D holes in strained Ge quantum wells
Von Känel, H.;Chrastina, D.;Isella, G.
2018-01-01
Abstract
The effective g-factor of 2D holes in modulation doped p-SiGe/Ge/SiGe structures was studied. The AC conductivity of samples with hole densities from 3.9 × 1011to 6.2 × 1011cm-2was measured in perpendicular magnetic fields up to 8 T using a contactless acoustic method. From the analysis of the temperature dependence of conductivity oscillations, the g⊥-factor of each sample was determined. The g⊥-factor was found to be decreasing approximately linearly with hole density. This effect is attributed to the non-parabolicity of the valence band.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
JApplPhys_123_165703.pdf
accesso aperto
:
Publisher’s version
Dimensione
891.59 kB
Formato
Adobe PDF
|
891.59 kB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.