Changes in transformation temperatures and high-temperature mechanical behavior of the new Ni50.6Ti34.4Hf25.0 alloy were determined after selected aging treatments. Differential scanning calorimetry was used to compare the homogenized, solution-treated and aged specimens for a wide combination of aging temperatures and times. Isothermal deformation experiments were conducted measuring reversible transformation strains with digital image correlation. Extraordinary superelasticity was found at test temperatures up to 300 °C for the specimen aged at 500 °C for 4 h.
High-temperature superelasticity of Ni50.6Ti24.4Hf25.0 shape memory alloy
PATRIARCA, LUCA;
2015-01-01
Abstract
Changes in transformation temperatures and high-temperature mechanical behavior of the new Ni50.6Ti34.4Hf25.0 alloy were determined after selected aging treatments. Differential scanning calorimetry was used to compare the homogenized, solution-treated and aged specimens for a wide combination of aging temperatures and times. Isothermal deformation experiments were conducted measuring reversible transformation strains with digital image correlation. Extraordinary superelasticity was found at test temperatures up to 300 °C for the specimen aged at 500 °C for 4 h.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
2015 Patriarca _ High-temperature superelasticity of NiTiHf SMAs.pdf
Accesso riservato
Descrizione: Articolo principale
:
Publisher’s version
Dimensione
957.84 kB
Formato
Adobe PDF
|
957.84 kB | Adobe PDF | Visualizza/Apri |
|
High-temperature superelasticity of NiTiHf SMAs_11311-1028873_Patriarca.pdf
accesso aperto
:
Post-Print (DRAFT o Author’s Accepted Manuscript-AAM)
Dimensione
961.68 kB
Formato
Adobe PDF
|
961.68 kB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.