The functionality of NiTiHf (25%Hf) shape memory alloy (SMA) was studied under isobaric temperature cycling experiments. Both the local and overall strains, determined with digital image correlation (DIC), displayed excellent stability and no measurable unrecovered elongation. The external stress levels were higher than 250 MPa and transformation temperature was 420 °C which exceeds other NiTi based alloys, demonstrating the outstanding potential of the NiTiHf alloys.
Shape memory functionality under multi-cycles in NiTiHf
PATRIARCA, LUCA
2017-01-01
Abstract
The functionality of NiTiHf (25%Hf) shape memory alloy (SMA) was studied under isobaric temperature cycling experiments. Both the local and overall strains, determined with digital image correlation (DIC), displayed excellent stability and no measurable unrecovered elongation. The external stress levels were higher than 250 MPa and transformation temperature was 420 °C which exceeds other NiTi based alloys, demonstrating the outstanding potential of the NiTiHf alloys.File in questo prodotto:
File | Dimensione | Formato | |
---|---|---|---|
2017 Sehitoglu _ Shape memory functionality under multi-cycles in NiTiHf.pdf
Accesso riservato
Descrizione: Articolo principale
:
Publisher’s version
Dimensione
673.35 kB
Formato
Adobe PDF
|
673.35 kB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.