For concrete structures exposed to corrosion, the identification of the local failure modes and of their occurrence in time represent an important information. This information is necessary in order to maintain a suitable level of system performance and to avoid collapse over the structural lifetime. In fact, repairable local failures can be considered as a warning of damage propagation and possible occurrence of more severe and not repairable failures. Failure loads and failure times are investigated and life-cycle probabilistic performance indicators, related to load redundancy and elapsed times between sequential failures, are proposed. The effects of the damage process on the structural performance are evaluated based on a methodology for life-cycle assessment of concrete structures exposed to diffusive attack from environmental aggressive agents. The uncertainties involved in the problem are taken into account in probabilistic terms. The proposed approach is illustrated through the application to a reinforced concrete frame and a reinforced concrete bridge deck under corrosion. The results demonstrate that both failure loads and failure times can provide relevant information to plan emergency procedures, repair interventions and maintenance actions in order to ensure suitable levels of life-cycle structural performance and functionality.

Failure Times of Concrete Structures in Aggressive Environment

BIONDINI, FABIO;
2014-01-01

Abstract

For concrete structures exposed to corrosion, the identification of the local failure modes and of their occurrence in time represent an important information. This information is necessary in order to maintain a suitable level of system performance and to avoid collapse over the structural lifetime. In fact, repairable local failures can be considered as a warning of damage propagation and possible occurrence of more severe and not repairable failures. Failure loads and failure times are investigated and life-cycle probabilistic performance indicators, related to load redundancy and elapsed times between sequential failures, are proposed. The effects of the damage process on the structural performance are evaluated based on a methodology for life-cycle assessment of concrete structures exposed to diffusive attack from environmental aggressive agents. The uncertainties involved in the problem are taken into account in probabilistic terms. The proposed approach is illustrated through the application to a reinforced concrete frame and a reinforced concrete bridge deck under corrosion. The results demonstrate that both failure loads and failure times can provide relevant information to plan emergency procedures, repair interventions and maintenance actions in order to ensure suitable levels of life-cycle structural performance and functionality.
2014
Life-Cycle of Structural Systems: Design, Assessment, Maintenance and Management
9781138001206
File in questo prodotto:
File Dimensione Formato  
2014_IALCCE.pdf

Accesso riservato

: Post-Print (DRAFT o Author’s Accepted Manuscript-AAM)
Dimensione 474.41 kB
Formato Adobe PDF
474.41 kB Adobe PDF   Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11311/946959
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 0
  • ???jsp.display-item.citation.isi??? 0
social impact