The microporous layer (MPL) is a key component of polymer electrolyte membrane fuel cells (PEM-FCs), and it is in charge of the gas and water management at the electrodegas diffusion layer (GDL) interfaces. A MPL was prepared and coated onto two different commercial GDLs: a carbon paper (woven-non-woven (WNW)) and a carbon cloth (CC). Electrical performances of the so-obtained gas diffusion media (GDM), i.e., GDL coated with the MPL, were investigated in single cell testing (steady-state polarization curves) using a Nafion® catalyst coated membrane with a platinum loading of 0.5 mg/cm2 both for the anode and the cathode. Moreover, in order to better understand the polarization phenomena during the running of the FC, impedance spectroscopy was carried out in galvanostatic mode at different current densities. In particular, the effect of the air relative humidity (RH 100%, 80%, and 60%) was investigated, while the hydrogen was fed always fully humidified (100%). The WNW substrate has demonstrated to be superior to CC in a vast range of current densities (from open circuit voltage to 0.8 A/cm2). However, at high current density, the WNW GDM has some problems in water management. ISI 5 PAGES

Electrical performance of PEM fuel cells with different gas diffusion layers

GALLO STAMPINO, PAOLA;DOTELLI, GIOVANNI
2011-01-01

Abstract

The microporous layer (MPL) is a key component of polymer electrolyte membrane fuel cells (PEM-FCs), and it is in charge of the gas and water management at the electrodegas diffusion layer (GDL) interfaces. A MPL was prepared and coated onto two different commercial GDLs: a carbon paper (woven-non-woven (WNW)) and a carbon cloth (CC). Electrical performances of the so-obtained gas diffusion media (GDM), i.e., GDL coated with the MPL, were investigated in single cell testing (steady-state polarization curves) using a Nafion® catalyst coated membrane with a platinum loading of 0.5 mg/cm2 both for the anode and the cathode. Moreover, in order to better understand the polarization phenomena during the running of the FC, impedance spectroscopy was carried out in galvanostatic mode at different current densities. In particular, the effect of the air relative humidity (RH 100%, 80%, and 60%) was investigated, while the hydrogen was fed always fully humidified (100%). The WNW substrate has demonstrated to be superior to CC in a vast range of current densities (from open circuit voltage to 0.8 A/cm2). However, at high current density, the WNW GDM has some problems in water management. ISI 5 PAGES
2011
File in questo prodotto:
File Dimensione Formato  
Electrical-performance-of-PEM-fuel-cells-with-different-gas-diffusion-layers_2011_Journal-of-Fuel-Cell-Science-and-Technology.pdf

Accesso riservato

: Post-Print (DRAFT o Author’s Accepted Manuscript-AAM)
Dimensione 609.33 kB
Formato Adobe PDF
609.33 kB Adobe PDF   Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11311/586273
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 18
  • ???jsp.display-item.citation.isi??? 15
social impact